Device isolation using preferential oxidation of the bulk substrate

ABSTRACT

A method includes providing a structure including a substrate, a buffer layer formed on the substrate and a semiconductor layer formed on the buffer layer, etching the semiconductor layer so as to form a fin and exposing the buffer layer, etching the buffer layer such that a portion of the buffer layer, disposed under the fin, is exposed, and oxidizing the buffer layer and fin so as to form an oxide layer under the fin.

The present application is a Divisional Application of U.S. patent application Ser. No. 14/213,511, filed on Mar. 14, 2014, the entire content of which are incorporated herein by reference.

FIELD OF THE INVENTION

The present invention generally relates to a semiconductor device having an oxide layer between a fin and the buffer layer. In particular, an aspect of the invention relates to a semiconductor device having a layer of InAlAs oxide between the InGaAs fin and the semiconductor buffer layer.

BACKGROUND OF THE INVENTION Description of the Related Art

InGaAs is a leading II-V candidate for a NMOS option in CMOS technology. InGaAs epi is usually grown on lattice matched InAlAs on InP. Although InAlAs is not intentionally doped, device isolation is a critical issue in the absence of a trench isolation technique, such as those is available in Si technology.

SUMMARY OF THE INVENTION

While InAlAs is a wide band-gap semiconductor, it is not entirely insulating. Thus, devices, such as transistors, built on an InAlAs substrate may be shorted or connected to each other through the InAlAs layer or through the substrate on which the InAlAs layer is grown. This creates a problem utilizing InAlAs as a medium on which to grow InGaAs epi out of which devices are built, as sufficient device isolation may not be achieved.

In view of the foregoing, and other, exemplary problems, drawbacks, and disadvantages of the conventional systems, it is an exemplary aspect of the present invention to provide a method and structure to realize sufficient device isolation.

In a first exemplary aspect of the invention, to achieve the above and other features and purposes, described herein is a structure including a semiconductor substrate, a semiconductor buffer layer disposed on the substrate, an oxide layer disposed on the buffer layer, and a fin comprising a semiconducting material disposed on the oxide layer wherein said fin and said buffer layer are epitaxially aligned to said substrate.

Another exemplary aspect of the invention is a method including providing a structure having substrate, a buffer layer formed on the substrate and a semiconductor layer formed on the buffer layer, etching the semiconductor layer so as to form a fin and exposing the buffer layer, etching the buffer layer such that a portion of the buffer layer disposed under the fin is exposed, and oxidizing the buffer layer and fin so as to form an oxide layer under the fin.

The above aspects may allow devices or fins to be isolated from the buffer layer.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing and other purposes, aspects and advantages will be better understood from the following detailed description of exemplary embodiments of the invention with reference to the drawings, in which:

FIG. 1 illustrates an exemplary embodiment of the starting structure;

FIG. 2 illustrates an exemplary embodiment in which fins are formed;

FIG. 3 illustrates a top view of exemplary FIG. 2;

FIG. 4 illustrates an exemplary embodiment after the buffer layer has been etched;

FIG. 5 illustrates an exemplary embodiment after the oxidation layer is formed;

FIG. 6 illustrates an exemplary method;

FIG. 7 illustrates another exemplary structure of the starting structure;

FIG. 8 illustrates another exemplary structure in which fins are formed;

FIGS. 9A-9C illustrate an exemplary process of forming the sidewalls;

FIG. 10 illustrates an exemplary structure after the sidewalls have been formed;

FIG. 11 illustrates an exemplary structure after the buffer layer has been etched;

FIG. 12 illustrates an exemplary structure after the oxidation layer is formed;

FIG. 13 illustrates an exemplary structure after the sidewalls are removed; and

FIG. 14 illustrates an exemplary method in which sidewalls are utilized.

DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENTS OF THE INVENTION

Referring now to the drawings, and more particularly to FIGS. 1-14, there are shown exemplary embodiments of methods and structures according to the present invention. It is noted that the Figures are not to scale.

An exemplary aspect of the invention proposes an isolation technique by local oxidation of an aluminum containing semiconductor by taking advantage of the differential oxidation rate of aluminum containing semiconductors compared to InGaAs. For example, the aluminum containing semiconductors include InAlAs, AlGaAs and AlAs. Using proper reaction conditions, such as in an environment of moist N2 (N2 passed through water at around 95° C.), an oxidation rate of InAlAs 10× to 80× faster than InGaAs is possible. In some instances, the oxidation rate of InAlAs can be 120× faster than InGaAs. Premchander Perumal et al.,” Investigations of the characteristics of strain-free oxidation on InAlAs epilayer lattice matched to indium phosphide” Appl. Phys. Lett. 88, 201914 (2006), H. Gebretsadik et al., “Lateral oxidation of InAlAs in InP-based heterostructures for long, and wavelength vertical cavity surface emitting laser applications”, Appl. Phys. Lett. 72 (2), 12 January (1998)

K. D. Choquette et al. “Advances in Selective Wet Oxidation of AlGaAs Alloys”, IEEE JOURNAL OF SELECTED TOPICS IN QUANTUM ELECTRONICS, VOL. 3(3), (1997) describe oxidation processes and are each incorporated herein by reference in their entirety.

By slightly undercutting the bottom of the fin, it is possible to oxidize the buffer layer under the fin, leading to a realization of a silicon-on-insulator (SOI) equivalent platform.

FIGS. 1-6 illustrate an exemplary embodiment of the invention. FIG. 6 illustrates an exemplary method and is described in reference to exemplary FIGS. 1-5.

FIG. 1 illustrates an Indium Gallium Arsenide (InGaAs) layer 1, formed on a buffer layer 2 of Indium Aluminum Arsenide (InAlAs) which is in turn formed on a substrate 3 of Indium Phosphide (InP) (S1). The InGaAs is a semiconductor compound that is latticed matched to the InP substrate when the indium composition is 53% (i.e., In_(0.53)Ga_(0.47)As). The InAlAs is latticed matched to the InP substrate when the indium content in the alloy is 50% (i.e. In_(0.5)Al_(0.5)As). Forming the InGaAs layer and the InAlAs layer is typically done using epitaxy (a process where the deposited crystal mimics the underlay substrate crystal structure). Typical epitaxial deposition methods include metal-organic molecular beam epitaxy (MOMBE) and metal-organic chemical vapor deposition (MOCVD).

In an exemplary embodiment of the invention, the fin and the buffer layer are epitaxially aligned to said substrate. In an exemplary embodiment of the invention, all of the semiconductor layers can be epitaxial (e.g., registered with respect to each other with the same crystal structure order and orientation).

A subtractive process (S2) is then performed, such as reactive-ion etching, in which part of the InGaAs layer is removed to form fins 4. An exemplary resultant structure is illustrated in FIGS. 2 and 3.

As shown in FIG. 4, buffer layer 2 is also etched so as to remove a portion of the InAlAs between the fins 4 such that the buffer layer 2 under fins 4 is exposed (S3).

In an embodiment, a portion of the buffer layer 2 located under fins 4 may also be removed.

The structure is then oxidized (S4), resulting in the structure of exemplary FIG. 5. In an exemplary embodiment, a preferential oxidation of the InAlAs is performed so that a layer of oxide 5 is formed underneath and between fins 4.

This process may be completed by using an oxidation process which is preferential to InAlAs. Such an oxidation process can oxidize InAlAs at many times the rate of the oxidation of InGaAs. For example, exemplary methods of oxidation allow the InAlAs to have an oxidation rate of eighty to one-hundred and twenty times that of InGaAs. Thus, a fin 4 may be isolated from the InAlAs layer 2 and the substrate 3.

As the InAlAs layer 2 was slightly etched, during the oxidation of the structure the sidewalls 8 of the InAlAs groove 9 adjacent to the fin 4 allows those sidewalls 8 to oxidize. In other words, because the side of InAlAs layer under the InGaAs is exposed, the portion of the InAlAs under the InGaAs can be effectively oxidized.

As shown in FIG. 5, because the oxidation rate of InAlAs is much greater than the oxidation rate of InGaAs, an oxidation layer 5 is formed under and between fins 4, while fins 4 are not substantially oxidized (e.g., the oxidation of fins 4 is minimal/negligible). In the exemplary embodiment, such as the embodiment of FIG. 5, the oxidation layer 5 extends under the entire width of fin 4 so that fin 4 is isolated from buffer layer 2 and the substrate 3.

In an exemplary embodiment, the oxidation is conducted so that the depth (D) of the oxidation layer 5 between fins 4 is the same as one halfthe width (W) of a fin 4. Alternatively, the depth (D) of the oxidation layer 5 between fins 4 can be slightly larger than one half the width (W) of a fin 4. Having a slightly larger depth to width ratio may help ensure that layer 5 (formed of oxidized InAlAs) is formed along the entire width (W) of fin 4. This can ensure that fin 4 is electrically isolated from InAlAs layer 2.

Another exemplary process, as illustrated in FIGS. 7-14, can provide further protection to the fins and/or can allow the oxidation process to be performed where preferential oxidation is not present. FIGS. 7-13 illustrate an exemplary structure, and FIG. 14 illustrates an exemplary method which will be described in reference to exemplary FIGS. 7-13.

Initially, a layered device such as that of FIG. 7 is provided (S21). The device may include a semiconductor layer 1 (e.g., InGaAs), buffer layer 2 (e.g., InAlAs), and substrate 3 (e.g., InP). The semiconductor layer is subjected to a subtractive process so as to produce fins 4 on a buffer layer 2 (S22). An exemplary result of an etching is shown in FIG. 8.

As shown in FIGS. 9A-9C, a sidewall layer 7 may be formed on fins 4 and buffer layer 2 (S23). The sidewall layer 7 can then be etched so as to remove a thickness of the sidewall layer 7 sufficient to expose the buffer layer 2 between fins 4 (S24). In one exemplary embodiment, once a certain thickness of layer 7 is removed, sidewalls 6 will naturally be formed adjacent fins 4.

The process for producing the sidewalls 6 is not particularly limited. For example, the sidewall layer 7 may be formed of silicon nitride or silicon dioxide. The sidewall layer 7 can be etched using a direction dry etching process, such as RIE, to form the sidewalls 6. Thus, the sidewalls 6 can be formed without the use of a mask.

After the sidewalls 6 are formed on fins 4, as shown in FIG. 10, the buffer layer 2 may be subjected to a subtractive process (e.g., etched) so as to expose a portion of the buffer layer 2 below the fins 4 (S25).

After the buffer layer 2 is etched, the structure can be oxidized (S26), the results of which may be seen in FIG. 12. Because the sides of fins 4 are covered with sidewalls 6, the sides of the fins 4 are protected from oxidation. Thus, the area of buffer layer 2 beneath and adjacent to the fins 4 is oxidized to form oxide layer 5 so as to isolate fins 4 from the layer buffer 2.

Because the sidewalls 6 protect fins 4 from oxidation this process does not require preferential oxidation of layer 2 versus fins 4. In other words, this process can be applied to materials other than InAlAs and InGaAs, or the process can be applied to InAlAs and InGaAs in oxidation environments which are not preferential to InAlAs. As a side note, the top of the fins 4 may be protected by the hard mask (not drawn) that was used to define the fins.

Alternatively, sidewalls 6 can be applied to fins 4 in a process using preferential oxidation in order to further protect the fins 4 from oxidation which the buffer layer is oxidized. Thus, the addition of sidewalls 6, as described above or by other known means, can be applied to fins 4 while using preferential oxidation in order to provide extra protection for fins 4, or the sidewalls 6 can be used as protection for fins 4 for processes which do not use preferential oxidation.

Once the oxidation process is completed, the sidewalls 6 can then be removed (S27), resulting in exemplary FIG. 13. The process for removing sidewalls 6 is not particularly limited. For example, sidewalls 6 can be removed using the same chemistry used by the etching process which formed sidewalls 6 from layer 7 but without the directionality. For example, the RIE process can be used with a lower bias and a higher pressure to render the etching process to be isotropic.

As a result of the exemplary processes, a structure may be formed where fins 4 are isolated from one another and buffer layer 2 through the use of oxide layer 5. An exemplary embodiment of such a structure is illustrated in FIGS. 5 and 13. In FIGS. 5 and 13, a buffer layer 2 is disposed on a substrate 3, an oxide layer 5 is disposed on the buffer layer 2, and one or more fins 4 are disposed on the oxide layer 5.

The materials used for each layer may vary and are not particularly limited. For a device formed using preferential oxidation (with or without sidewalls), the substrate 1 may be formed of InP, the buffer layer 2 may be formed of InAlAs, the oxide layer 5 may be formed of an oxide of InAlAs (e.g., Al₂O₃), and fins 4 may be formed of InGaAs.

In other embodiments, the substrate 1 may be formed of GaAs, the buffer layer 2 may be formed of AlGaAs, the oxide layer 5 may be formed of Al₂O₃ and fins 4 may be formed of GaAs. Such a structure may be formed using preferential oxidation, sidewalls 6, or both, as noted above.

In FIGS. 5 and 13, it can be seen that oxide layer 5 isolates the fins 4 from the buffer layer 2 and the substrate 3. Interconnects may also be formed between fins 4 on oxide layer 5, as desired, using conventional methods.

The dimensions of the layer thicknesses and width of the fin can vary depending on the particular needs of the device and the relative oxide rates of the layers. For instance, in some applications the buffer layer 2 may be formed of InAlAs with a thickness from 10 nm to 500 nm, with a more typical thickness of around 100 nm. Fins 4 may be formed of InGaAs having a thickness of 10-100 nm, depending on the application. In an exemplary embodiment, if the width of the fins 4 is 30 nm, for example, then the oxide layer 5 may be approximately 15-20 nm thick, assuming a constant rate of oxidation on all exposed surfaces of the buffer layer 2.

While the invention has been described in terms of exemplary embodiments, those skilled in the art will recognize that the invention can be practiced with modification within the spirit and scope of the appended claims.

Further, it is noted that, Applicant's intent is to encompass equivalents of all claim elements, even if amended later during prosecution. 

1. A method, comprising: providing a structure including a substrate, a buffer layer formed on the substrate and a semiconductor layer formed on the buffer layer; etching the semiconductor layer so as to form a fin and exposing the buffer layer, etching the buffer layer such that a portion of the buffer layer, disposed under the fin, is exposed; and oxidizing the buffer layer and fin so as to form an oxide layer under the fin.
 2. The method according to claim 1, wherein the oxidizing the buffer layer is performed such that the oxide layer extends from one side of the fin to another side of the fin in a width direction.
 3. The method according to claim 1, wherein, in a width direction, a portion of the fin has the oxide layer formed under an entirety of the portion of the fin.
 4. The method according to claim 1, wherein the oxidizing comprises performing the oxidizing of the buffer layer and fin in an environment such that the buffer layer oxidizes faster than the fin.
 5. The method according to claim 1, wherein the buffer layer and the fin are oxidized at a same time.
 6. The method according to claim 1, further comprising: after etching the semiconductor layer, forming a sidewall adjacent the fin.
 7. The method according to claim 6, wherein the forming the sidewall further comprises: forming a protective layer over the fin and the buffer layer, and etching the protective layer such that the buffer layer is exposed and the sidewall is formed from the protective layer adjacent the fin.
 8. The method according to claim 1, wherein the oxide layer directly contacts the fin and the buffer layer.
 9. The method according to claim 1, wherein the oxide layer comprises an oxide of the buffer layer.
 10. The method according to claim 1, wherein the oxide layer is sandwiched between the buffer layer and the fin.
 11. The method according to claim 1, wherein the substrate comprises InP, the buffer layer comprises InAlAs, and the semiconductor layer comprises InGaAs.
 12. The method according to claim 1, wherein the semiconductor layer is lattice matched with the buffer layer.
 13. The method according to claim 1, wherein the fin is lattice matched with the buffer layer.
 14. The method according to claim 1, wherein the fin comprises a III-V compound and the buffer layer comprises a III-V compound. 